FLUID FILM MULTI FILM 1 liter BLACK

HODT MULTI FILM protects and preserves as a compact coating material as well as a primer and top coat.

• 1 liter black
• Compact coating material
• Protects and preserves
• Solves many rust protection problems

Features

• HODT MULTI FILM is an aqueous emulsion with mild odor, low VOC content and very low toxicity.
  It is a non-hazardous and environmentally friendly alternative to solventborne topcoats and corrosion inhibitors at a dry film thickness (dft) > 100 μm.
  1-component product with excellent adhesion and elasticity, rapid oxidative drying, water resistance and recoatability.
  Suitable substrates: organic coatings, grease-free iron, galvanized steel, aluminum, cement plaster, plastic plaster, concrete, plastic, emulsion paint coatings, etc.
  Economical to use and uncomplicated to apply. In one operation, a layer thickness of
  50 to 80 μm can be applied (by spraying and dipping).
  Can be diluted with water as desired, which results in a much greater reduction in viscosity
  than in the case of synthetic resins with organic solvents; the product meets the highest requirements in terms of chemical
  and mechanical resistance. It adheres to natural and synthetic rubber, polyethylene, PVC.
  The water-based clear coat also meets the strict environmental requirements.
  High elasticity of the coating ensures that no cracking or chipping occurs during expansion or contraction of the substrate.
  contraction of the substrate metal.
  As an oxidatively drying coating, HODT MULTI FILM must, as with alkyd products, absorb oxygen for curing.
  for curing. It is therefore not sufficient for the water in the emulsion to evaporate and form a film (so-called anti-drying),
  additional drying time must be allowed for the absorption of oxygen in order to obtain a fully loadable coating.
  coating is obtained.
  Although HODT MULTI FILM is highly resistant to solvents, i.e. it can be used as a primer for other coatings, it is advisable to use it as a primer for other coatings.
  it is advisable to perform a resistance test on a small area before such an application.

Mode of operation:

• The substrate for HODT MULTI FILM must be free of grease!
• When applying HODT MULTI FILM by brush, roller, dipping or spraying, always apply "dry on dry" (after approx. 2 hours) to obtain a film thickness of approx. 120 - 160 μm.
• For spraying, HODT MULTI FILM can be diluted with water if necessary.
• However, after dilution, more coats must be applied to create the desired optimum film thickness.
• This drying time depends on the temperature. Forced drying at a temperature of 50 - 60 °C can reduce the drying time to 2 -3 hours.
• On the other hand, at a normal temperature of approx. 20°C, a drying time of 24 hours must be expected before further coats of HODT MULTI FILM or other paints can be applied to the multifilm coating.

Technical Merkmale:

• Temperature range (in °C): -40°C to 120°C (+150° short).
• Touch dry: (at 20 °C u. 25 μm film thickness): 2 hrs.
• Curing time (at 20 °C in hours): 24
• Solvent resistance: good
• Moisture resistance: good
• Thinner: water
• also available in aerosol: no
• Color: clear / black
   
• Dynamic viscosity: (10 1/s; 23 °C) DIN EN ISO 3219 10000 mPa.sek
• Flash point (in liquid form): not applicable
• Solids content (wt%): 34-36
• Spec. weight: 1.02 g/cm³
• Salt spray test according to DIN EN ISO 9227 Duration 480 h